tensile strength的例句大全

Results showed appropriate boric oxide would improve the tensile strength of SiO2-Al2O3-MgO fiberglass, and perfect the processing property through reducing the high temperature viscosity of the glass.

其中引入氧化硼的研究结果表明，氧化硼引入量从1wt.%增加到2wt.%时可提高硅铝镁系高强玻纤拉伸强度200MPa左右，通过降低玻璃液的高温粘度为其工艺性能的改善提供了可能。

互联网摘选

When the brazing temperature exceeded 650 ℃, the tensile strength decreased.

温度高于650℃，抗拉强度降低；

互联网摘选

The strength properties of these paper are better, on 30 ° SR of beating degree, the tensile index are 59.4 N · m/ g to 63.7 N · m/ g.

纸浆的强度性能良好，叩解度为30°SR时，其抗张指数为59.4～63.7N·m/g。

互联网摘选

Results showed that with the increase of flame retardant additives, the breaking strain, tensile strength and elongation at break declined, but the elasticity modulus increased.

结果显示：随阻燃剂添加量增加，体系的扯断应变、拉伸强度、断裂伸长率下降，弹性模量增大。

互联网摘选

OUR MICRO-FIBER WIPER IS MADE VERY SOFT AND HIGH TENSILE STRENGTH.

敝公司专门生产无尘擦拭布,适用于精密电子或光学产品,如电子零件、动元件、C产品擦拭使用.

互联网摘选

The advantages of our rubber mat include high tensile strength, excellent abrasive resistant, various patterns etc.

我们生产的橡胶板高强力, 高耐磨, 花纹多样.

互联网摘选

The Relation Between Incipient Cavitation and Tensile Strength of a Liquid

初生空化与液体抗拉强度的关系

互联网摘选

Multi types and sizes of bead wire with high tensile strength should be developed.

胎圈钢丝要发展多品种、多规格和高强度产品.

互联网摘选

Compared to the normal wire drawing technology in room temperature, the cryogenic wire drawing technology showed remarkable effect: tensile strength was improved nearly 400 MPa, micro vickers hardness was enhanced 74 HV 4.9N, in the meanwhile, toughness was almost changeless.

研究表明，在相同的拉丝条件下，与常温工艺相比，深冷工艺能大幅度提高钢丝的综合力学性能。抗拉强度进一步提高近400MPa，显微硬度进一步提高74HV4.9N，而抗扭次数及伸长率基本不变。

互联网摘选

The results of experiments indicate that although the tensile strength of the melt extracted steel fibre is lower than that of cutting cold draw wire, the melt extracted steel fibre can be used to reinforce the conventional concrete.

实验表明，尽管熔抽钢纤维的抗张强度低于切割冷拉丝钢纤维，但熔抽钢纤维仍可用来强化常规混凝土。

互联网摘选

The water solubility, broken tensile strength of blend nano-fibers were tested and analyzed.

同时对纤维网的水溶性、断裂强度、断裂伸长率等进行了测试和分析。

互联网摘选

The water solubility, broken tensile strength of blend nano-fibers were tested and analyzed.

同时对纤维网的水溶性、断裂强度、断裂伸长率等进行了测试和分析。

互联网摘选

The mechanical properties of NaCS film were significantly influenced by NaCS Mw, however, were less influenced by NaCS DS. The tensile strength and elongation at break would decrease when carrageenan or agar was added in NaCS film.

研究发现NaCS分子量对膜的拉伸强度和断裂伸长率影响较大，而NaCS取代度则对其影响较小。在NaCS膜中加入卡拉胶或琼脂后，膜的力学性能会下降。

互联网摘选

Experimental results of Marshall Remnant Stability Test, Water Susceptibility Tensile Strength Ratio ( TSR) Test and Rutting Test show that graphite modified ECAC possesses of high anti-water damage ability and excellent high-temperature stability, which is expected to apply as new-type pavement.

马歇尔残留稳定度试验、冻融劈裂试验和车辙试验表明石墨导电沥青混凝土的抗水损害能力强，高温稳定性能良好，可作为新型路面使用。

互联网摘选

The results indicated that when a straight rube is formed into a spiral tube, its stress distribution becomes complicated, and both tensile stress and pressure stress exist and their directions are not in the same direction though the bursting strength will not decrease.

结果表明：光管成型加工成螺旋管后，虽然爆破强度不会下降，但其应力分布变得复杂，既存在拉应力又存在压应力，且方向也不一致。

互联网摘选

The results show that grains can be obviously refined by CCDC same as other SPD technologies. The microhardness and tensile strength increase obviously, but the elongation to failure and electrical conductivity decrease.

实验结果表明：反复镦压与其他剧烈塑性变形技术一样能使纯铜的晶粒明显细化，纯铜的硬度和抗拉强度明显提高，但断后伸长率和电导率下降。

互联网摘选

By Cr microalloying, the fore eutectoid ferrite eduction is restrained, the distance between rows of pearlite is decreased, then the tensile strength, section shrinkage and drawing property of high carbon steel wire rod is obviously raised and improved.

高碳钢中加入的铬元素抑制先共析铁素体析出，减小珠光体片层间距，可明显提高抗拉强度，提高断面收缩率，改善线材的拉拔性能。

互联网摘选

The results indicated that with the increase of the content of the extender oil, the tensile strength decreased, while the elasticity increased and elongation at break improved.

结果表明：随着填充油用量的增加，拉伸强度下降，弹性回复增加，断裂伸长率也增大。

互联网摘选

Selection and Control of Tensile Strength of Aluminium Wires in ACSR

钢芯铝绞线铝单线抗拉强度的选择及控制

互联网摘选

The tensile strength and the bending modulus of RHDPE/ EVA/ MWRP blend increased by 35% and 25% respectively when the waste rubber powder was modified by self-made surface modifier ACDI.

废胶粉经自制表面改性剂ACDI预处理后，其相应的RHDPE/EVA/MWRP体系的拉伸强度和弯曲模量分别增加35%和25%，而对共混物的其它性能影响不大。

互联网摘选